钠电产品全品类目录

产品类型: 100 %聚阴离子正极 应用: 2 场景：储能/动力钠电池

{"D10":"μm （典型值 2.79）","D50":"μm （典型值 9.11）","D90":"μm （典型值 17.80）","pH":"（典型值 9.86）","Na2CO3":"wt% （典型值 1.47）","NaOH":"wt% （典型值 0.12）","C":"wt% （典型值 1.95）","BET":"m²/g （典型值 8.23）","CP Density":"g/cc （典型值 1.53）","Tap Density":"g/cc （典型值 2.08）","0.2C 充电比容量(扣式)":"mAh/g （典型值 115.70）","0.2C 放电比容量(扣式)":"mAh/g （典型值 103.60）","0.2C 首效(扣式)":"% （典型值 89.50）","软包 0.2C 比容量":"mAh/g （典型值 96.60）","软包 0.5C 比容量":"mAh/g （典型值 94.30）","软包 1C 比容量":"mAh/g （典型值 92.50）"}

{"D10":"≥2.00 μm （典型值 2.92）","D50":"11.50±2.50 μm （典型值 11.23）","D90":"<26.00 μm （典型值 16.85）","pH":"≤13.40 （典型值 12.73）","Na2CO3":"<2.50 wt% （典型值 1.16）","NaOH":"<0.50 wt% （典型值 0.19）","BET":"0.55±0.15 m²/g （典型值 0.53）","CP Density":"≥3.15 g/cc （典型值 3.20）","Tap Density":"≥1.50 g/cc （典型值 2.19）","0.2C 充电比容量":"≥158.90 mAh/g （典型值 154.90）","0.2C 放电比容量":"≥143.00 mAh/g （典型值 143.20）","0.2C 首效":"≥90.00 % （典型值 92.40）"}

{"D10":">3.00 μm （典型值 4.20）","D50":"10.50±3.50 μm （典型值 7.90）","D90":"<26.00 μm （典型值 13.00）","pH":"≤13.50 （典型值 12.90）","Na2CO3":"<2.00 wt% （典型值 0.66）","NaOH":"<0.30 wt% （典型值 0.11）","BET":"0.70±0.20 m²/g （典型值 0.63）","CP Density":"g/cc （典型值 3.03）","Tap Density":"1.90±0.30 g/cc （典型值 1.84）","0.2C 充电比容量":"mAh/g （典型值 143.30）","0.2C 放电比容量":"130.00±5.00 mAh/g （典型值 132.70）","0.2C 首效":"≥90.00 % （典型值 92.60）"}

{"D10":"≥2.00 μm （典型值 4.20）","D50":"7.50±2.50 μm （典型值 7.86）","D90":"≤26.00 μm （典型值 13.72）","pH":"≤13.50 （典型值 12.52）","Na2CO3":"<3.00 wt% （典型值 0.83）","NaOH":"≤1.50 wt% （典型值 0.22）","BET":"0.70±0.20 m²/g （典型值 0.68）","CP Density":"g/cc （典型值 2.90）","Tap Density":"1.70±0.30 g/cc （典型值 1.88）","0.2C 充电比容量":"mAh/g （典型值 152.60）","0.2C 放电比容量":"≥135.00 mAh/g （典型值 139.10）","0.2C 首效":"≥90.00 % （典型值 91.10）"}

晶型和成分 类单晶 Ni 20 mol% | 电化学性能 首效＞94% 0.1C＞133 mAh/g 1C ＞125 mAh/g | 应用领域 动力、储能

比表面积m2/g 9.32 | 3T粉末压实密度/g/cc 1.99 | 极片压实密度/g/cc 2.25 | 碳含量(%) 1.32 | 0.2C充电容量(mAh/g)(2.0-3.6V) 113.00 | 0.2C放电容量(mAh/g)(2.0-3.6V) 101.00 | 首周效率(%) 90.00 | 1C/0.2C容量保持率(%) 97.00 | 5C/0.2C容量保持率(%) 85.00

比表面积m2/g 9.74 | 3T粉末压实密度/g/cc 1.97 | 极片压实密度/g/cc 2.00 | 碳含量(%) 1.75 | 0.2C充电容量(mAh/g)(2.0-3.6V) 113.00 | 0.2C放电容量(mAh/g)(2.0-3.6V) 101.00 | 首周效率(%) 90.00 | 1C/0.2C容量保持率(%) 98.00 | 5C/0.2C容量保持率(%) 90.00

晶型和成分 多晶 Ni 33 mol% | 电化学性能 首效＞95% 0.1C＞144 mAh/g 1C ＞134 mAh/g | 应用领域 两轮车

D10：0.3µm D50：1.3µm D90：2.2µm BET：22 m2/g TD：0.8g/cm3 电池性能：1.7~4.3V，0.1C倍率112mAh/g，1C倍率105mAh/g

D10：8.4µm D50：11.9µm D90：15.3µm BET：1.3 m2/g TD：1.9g/cm3 电池性能：2.0~4.0V，0.1C倍率135mAh/g，1C倍率125mAh/g